Aliphatic
Acrylic Urethane Gloss M74/75,
CM74/75
|
|
MSDS |
Technical
Data Sheet |
Product
Information
This two component acrylic urethane provides
excellent chemical & abrasion resistance, plus
color and gloss retention. The cured coating
equals the results of the best baking finishes.
This coating performs well on high trafficked
floors where color and gloss are desired. Resists
continuous clean with strong cleaning compounds.
Resists the strong solvents used in graffiti
removal. Curing time may be accelerated or
retarded as necessary by the addition of M77
Urethane Accelerator or M92 Urethane Retarder.
Recommended Uses
Buildings, Cement trucks, airplanes, waste
treatment plants, machinery, food processing
plants, rolling stock, chemical plants,
construction equipment, pulp and paper mills,
highway and mining equipment, fertilizer plants,
lockers, breweries, storage tanks, power
generating plants, bridges, oil field equipment,
towers, bottling plants
Colors: Clear,
Safety Yellow, Safety Red, Safety Blue, Safety
Orange, Safety Black, Tintable White, Tinting
base, Clear base
|
|
| Technical
Data |
White |
| Generic
Type |
Aliphatic
Acrylic Urethane |
| Pigment
Type |
TiO2 |
| Volume
Solids |
52%
mixed
(54%) |
| Spread
Rate per Gal. |
420
Sq. Ft. |
Film
Thickness
- Wet
- Dry |
3.8
mils
2.0 mils |
Dry
Time
- To Touch
- Recoat |
2
hours
4-8 hours |
| Dry
Heat Resistance |
250°
F |
| Viscosity |
75
± 5 KU |
| Flash
Point (Seta) |
86°
F
(84° F) |
| 60°
Specular Gloss |
90% |
| Clean
Up With |
M93 |
| Mixing
Ratio |
4:1
by volume |
| Induction
Time |
30
minutes |
| Pot
Life @ 70° F |
6-8
hours |
|
| |
|
| Aliphatic
Acrylic Urethane Gloss Clear Finish CM74-00/75 |
| MSDS |
Technical
Data Sheet |
Product
Information
This two component acrylic urethane provides
excellent chemical & abrasion resistance, plus
color and gloss retention. The cured coating
equals the results of the best baking finishes.
This coating performs well on high trafficked
floors where color and gloss are desired. Resists
continuous clean with strong cleaning compounds.
Resists the strong solvents used in graffiti
removal. Curing time may be accelerated or
retarded as necessary by the addition of M77
Urethane Accelerator or M92 Urethane Retarder.
Recommended Uses
Buildings, walls, floors, showers, kitchens,
ceramic tile, clear floor coating for easy stain
removal, non-yellowing clear to facilitate
graffiti removal, high traffic floors |
|
| Technical
Data |
|
| Generic
Type |
Aliphatic
Acrylic Urethane |
| Pigment
Type |
Inert |
| Volume
Solids |
44%
mixed
(54%) |
| Spread
Rate per Gal. |
360
Sq. Ft.
(425 Sq. Ft.) |
Film
Thickness
- Wet
- Dry |
4.5
(3.8) mils
2.0 mils |
Dry
Time
- To Touch
- Recoat |
2
hours
4-8 hours |
| Dry
Heat Resistance |
250°
F |
| Viscosity |
60
± 5 KU |
| Flash
Point (Seta) |
83°
F |
| 60°
Specular Gloss |
90% |
| Clean
Up With |
M93 |
| Mixing
Ratio |
4:1
by volume |
| Induction
Time |
30
minutes |
| Pot
Life @ 70° F |
6-8
hours |
|
| |
|
| Moisture
Cured Urethane Clear M78, CM78 |
| MSDS |
Technical
Data Sheet (pdf) |
Product
Information
This single component moisture cured urethane
clear reacts with the moisture in the air cross
linking the liquid into a tough, flexible,
resilient coating. Provides excellent abrasion
resistance and good chemical resistance on wood or
concrete surfaces that are exposed to high abuse.
Performs well as sealer or finish on warehouse
floors and aisles. Stops dusting and staining;
improves housekeeping.
Recommended Uses
High abuse areas of wood, manufacturing areas,
concrete floors and aisles, gym floors, warehouses
Colors:
Clear
|
|
| Technical
Data |
|
| Generic
Type |
Moisture
Cured Urethane |
| Pigment
Type |
Clear |
| Volume
Solids |
36%
(49%) |
| Spread
Rate per Gal. |
290
Sq. Ft.
(390 Sq. Ft.) |
Film
Thickness
- Wet
- Dry |
5.6
(4.1) mils
2.0 mils |
Dry
Time
- To Touch
- Recoat |
1
hours (2 hours)
4 hours (16 hours) |
| Dry
Heat Resistance |
250°
F |
| Viscosity |
30
sec. #2 Zahn
40 sec. #2 Zahn |
| Flash
Point (Seta) |
81°
F |
| 60°
Specular Gloss |
80% |
| Clean
Up With |
M94 |
| Mixing
Ratio |
N/A |
| Induction
Time |
N/A |
| Pot
Life @ 70° F |
N/A |
|
| |
|
| Urethane
Accelerator M77 |
| MSDS |
|
Product
Information
Accelerates cure time of 2-component aliphatic
urethanes. Improves recoat time. á Minimizes dust
and dirt pickup. Reduces dry-to-touch time from 2
hours to 1 hour. Reduces dry-to-recoat time from 6
hours to 3 hours. Flash point 84° F
Will raise the VOC level of the product to which
it is added. Refer to individual product data
sheets for specific details. The Specifier should
be aware that a number of jurisdictions in the USA
now regulate the VOC content of Industrial
Coatings. Thinning of this product will make it
non-compliant under normal environmental and
application conditions in VOC regulated areas.
Local authorities should be consulted for updated
regulations.
Recommended Uses
Intended for use with M74/M75, CM74/M75, and
DM74/DM75 Aliphatic Acrylic Urethane |
|
|
| |
|
| Urethane
Retarder M92 |
| MSDS |
|
Product
Information
Lengthens pot life and dry time of 2-component
aliphatic urethanes by up to 100%. Improves flow
and leveling properties of when applied by brush
or roller.
Increases dry time by 1- 2 hours. Flash point 108°
F
Recommended Uses
Intended for use with M74/M75 Aliphatic Urethane,
this blend of retarding solvents will improve flow
and leveling during brush and roller application.
Not for use with
DM74/DM75. The Specifier should be aware that a
number of jurisdictions in the USA now regulate
the VOC content of Industrial Coatings. Thinning
of this product will make it non-compliant under
normal environmental and application conditions in
VOC regulated areas. Local authorities should be
consulted for updated regulations. Maximum
allowable addition to CM74/M75 is 2 fl. oz., per
gallon, in 420 VOC areas; 8 fl. oz. in 450 VOC
areas.
|
|
|
|
|
|